Prototype Engineering Series: MSLA Heat Resin Gray, for LCD Masked Printers

×
×
RRP:
$99.00
Your Price:
$90.00 (You save $9.00)
Quantity:

Product Description

MSLA Heat Resin is our first engineering resin for LCD masked printers with a heat deflection temperature (HDT) of 250oC at 0.45 MPa. It is ideal for prototype parts that will come in contact with high temperature. MSLA Heat Resin prints precise models, holds its shapes with high thermal stability.

Product Features 

  • For all LCD masked printers, such as Phrozen, AnyCubic…etc.
  • Print Layer Thickness: 100, 50 microns
  • Tensile Strength (60-80 MPa) / Elongation (1-3%)
  • Minimum odor
  • SKU: MPT-HE001GY
  • For detailed print instructions, please refer to Printing Tips

  

Material Properties Table

MSLA-Heat Gray MPT-HE001GY
Post-curing FormCure at
35℃/60min
FormCure at
60℃/60min + oven 160℃/90min
Tensile (MPa) 55 - 75 60 - 80
Elongation (%) 1 - 2 1 - 3
Impact (J/m) 19 - 25 24 - 31
Hardness (Shore) 85 - 87 D 87 - 89 D
Flexure strength (MPa) 130 - 145 135 - 185
Flexure modulus (MPa) 2550 - 2650 2850 - 3000
HDT (℉/℃) 228.2/109 482/250 *
Viscosity (cP) 450 - 550
  * FormCure at 80℃/120min + oven 160℃/180min

Product Details

Color: Gray
Size: 1 Liter
Material: Acrylate-based Polymer for 3D Printing
Tensile(MPa): 55 - 75
Elongation(%): 1 - 2
Impact(J/m): 19 - 25
Hardness(Shore): 85 - 87D
Flexural Strength(MPa): 130 - 145
Flexural Modulus(MPa): 2550 - 2650
HDT(°F/°C): 228.2/109
Tear Strength(kN/m): -
Compression(%): -
Viscosity (cP): 450 - 550
      

    Material Properties Table

    MSLA-Heat Gray MPT-HE001GY
    Post-curing FormCure at
    35℃/60min
    FormCure at
    60℃/60min + oven 160℃/90min
    Tensile (MPa) 55 - 75 60 - 80
    Elongation (%) 1 - 2 1 - 3
    Impact (J/m) 19 - 25 24 - 31
    Hardness (Shore) 85 - 87 D 87 - 89 D
    Flexure strength (MPa) 130 - 145 135 - 185
    Flexure modulus (MPa) 2550 - 2650 2850 - 3000
    HDT (℉/℃) 228.2/109 482/250 *
    Viscosity (cP) 450 - 550
      * FormCure at 80℃/120min + oven 160℃/180min
!-->
  • Product Details

    Color: Gray
    Size: 1 Liter
    Material: Acrylate-based Polymer for 3D Printing
    Tensile(MPa): 55 - 75
    Elongation(%): 1 - 2
    Impact(J/m): 19 - 25
    Hardness(Shore): 85 - 87D
    Flexural Strength(MPa): 130 - 145
    Flexural Modulus(MPa): 2550 - 2650
    HDT(°F/°C): 228.2/109
    Tear Strength(kN/m): -
    Compression(%): -
    Viscosity (cP): 450 - 550
  • ×
    ×