Laser Resins

Laser Resins

 
 

MODELING
200
GRAY
 

MODELING
BLACK V2
 

MODELING
CLEAR
 

MODELING
GRAY
 

MODELING
WHITE
 

MODELING
TAN
 

EXPERT
BLACK
 

ROBUST
CHAMPAGNE
 

SPRING
BLACK
 

SPRING
PINK
Group
Tensile(MPa) 57-59 47-52 53-63 50-55 46-53 40-44 70-80 45-55 1.2-1.3 1.1-1.2
Elongation(%) 3-7 2-6 1-4 2-4 1-3 2-6 1-3 10-21 45-55 40-55
Impact(J/m) 43-44 16-22 17-29 15-17 23-27 15-17 35-40 60-65 - -
Hardness(Shore) 86-88D 86-88D 85-88D 85-87D 85-90D 84-86D 88-90D 83-86D 57-60A 56-59A
Flexure Strength(MPa) 92-104 82-86 89-105 89-95 90-105 79-83 115-150 65-90 - -
Flexure Modulus(MPa) 1700-2000 2050-2150 1600-2000 2250-2470 1550-1750 1970-2190 2050-2500 1000-1500 - -
HDT(°F/°C) - 135.86/57.7 170.60/77.0 135/57 170.78/77.1 131/55 154.04/67.8 125.78/52.1 - -
Viscosity(cP) 675-825 1000-1200 1100-1300 1000-1300 900-1050 1000-1200 1050-1200 1300-1500 500-600 480-550
Compression Set(%) - - - - - - - - 1.5-2.5 1.5-2.5

 


 

 
 
HEAT
Champagne
Group
Post-curing FormCure at
60℃/60min
FormCure at
60℃/60min + oven 160℃/90min
Tensile(MPa) 65 - 80 65 - 85
Elongation(%) 1 - 3 1 - 2
Impact (J/m) 16 - 27 23 - 39
Hardness (Shore) 86 - 88 D 86 - 88 D
Flexure strength (MPa) 140 - 160 150 - 180
Flexure modulus (MPa) 2550 - 2750 2950 - 3100
HDT (℉/℃) 213.8/101 370.4/188 *
Viscosity (cP) 550 - 650
  * FormCure at 80℃/120min + oven 160℃/180min

 

3D Printing Material Groups

Design Concept

Visual Aid for discussion & evaluation

Read more

Prototype Engineering

Simulates ABS,
PE, Rubber ......

Read more

Functional Engineering

Products that outperforms conventional manufacturing

Coming Soon

Specialty

Specific workflow, Specific application, …

Coming Soon

Material Properties Table

For Laser Printer Resins

 
 

MODELING
200
GRAY
 

MODELING
BLACK V2
 

MODELING
CLEAR
 

MODELING
GRAY
 

MODELING
WHITE
 

MODELING
TAN
 

EXPERT
BLACK
 

ROBUST
CHAMPAGNE
 

SPRING
BLACK
 

SPRING
PINK
Group
Tensile(MPa) 57-59 47-52 53-63 50-55 46-53 40-44 70-80 45-55 1.2-1.3 1.1-1.2
Elongation(%) 3-7 2-6 1-4 2-4 1-3 2-6 1-3 10-21 45-55 40-55
Impact(J/m) 43-44 16-22 17-29 15-17 23-27 15-17 35-40 60-65 - -
Hardness(Shore) 86-88D 86-88D 85-88D 85-87D 85-90D 84-86D 88-90D 83-86D 57-60A 56-59A
Flexure Strength(MPa) 92-104 82-86 89-105 89-95 90-105 79-83 115-150 65-90 - -
Flexure Modulus(MPa) 1700-2000 2050-2150 1600-2000 2250-2470 1550-1750 1970-2190 2050-2500 1000-1500 - -
HDT(°F/°C) - 135.86/57.7 170.60/77.0 135/57 170.78/77.1 131/55 154.04/67.8 125.78/52.1 - -
Viscosity(cP) 675-825 1000-1200 1100-1300 1000-1300 900-1050 1000-1200 1050-1200 1300-1500 500-600 480-550
Compression Set(%) - - - - - - - - 1.5-2.5 1.5-2.5

 


 

 
 
HEAT
Champagne
Group
Post-curing FormCure at
60℃/60min
FormCure at
60℃/60min + oven 160℃/90min
Tensile(MPa) 65 - 80 65 - 85
Elongation(%) 1 - 3 1 - 2
Impact (J/m) 16 - 27 23 - 39
Hardness (Shore) 86 - 88 D 86 - 88 D
Flexure strength (MPa) 140 - 160 150 - 180
Flexure modulus (MPa) 2550 - 2750 2950 - 3100
HDT (℉/℃) 213.8/101 370.4/188 *
Viscosity (cP) 550 - 650
  * FormCure at 80℃/120min + oven 160℃/180min

 