MSLA Resins

MSLA Resins

 
 
MODELING
GRAY
 
MODELING
DENTAL
 
MODELING
CLEAR
 
CASTABLE
CYAN
Group
Tensile(MPa) 52 - 60 47 - 55 53 - 67 6 - 7
Elongation(%) 2 - 4 1 - 4 1 - 3 7 - 9
Impact(J/m) 20 - 28 18 -26 29 -31 -
Hardness(Shore) 89 - 92D 86 - 90D 85 - 88D -
Flexure Strength(MPa) 92 - 100 92 - 96 95 - 105 6 - 8
Flexure Modulus(MPa) 2100 - 2300 2100 - 2300 1800 - 2000 90 - 120
HDT(°F/°C) 140.36/60.2 137.84/58.8 149.54/65.3 -
Viscosity(cP) 310 - 380 300 - 370 360 - 450 300 - 350

 


 

 
 
HEAT
GRAY
 
EXPERT
GRAY
 
RIGID
DUSTY OLIVE
 
SPRING
BLACK
 
SPRING
PINK
Group
Post-curing FormCure at
35℃/60min
FormCure at
60℃/60min + oven 160℃/90min
- - - -
Tensile(MPa) 55 - 75 60 - 80 65 - 74 55 - 60 1.2 - 1.8 1.2 - 1.8
Elongation(%) 1 - 2 1 - 3 3 - 6 8 - 12 45 - 65 50 - 70
Impact (J/m) 19 - 25 24 - 31 25 - 27 40 - 45 - -
Hardness (Shore) 85 - 87 D 87 - 89 D 91 - 93 D 89 - 92D 57 - 62A 58 - 62A
Flexure strength (MPa) 130 - 145 135 - 185 110 - 130 85 - 100 - -
Flexure modulus (MPa) 2550 - 2650 2850 - 3000 2200 - 2400 1600 - 1800 - -
HDT (℉/℃) 228.2/109 482/250 * 160.9/71.6 147.4/64.1 - -
Viscosity (cP) 450 - 550 600 - 700 650 - 800 480 - 520 480 - 520
  * FormCure at 80℃/120min + oven 160℃/180min        
25℃ density(g/cm3)(cP) - - - - 1.11 - 1.12 1.11 - 1.12
Tear Strength (kN/m) - - - - 3 - 5 3 - 5
Compression (%) - - - - 1 - 2 1 - 2
Layer thickness(um) - - 0.1 mm - - -
PostCure method) - - Elegoo Mercury 30 min - - -

3D Printing Material Groups

Design Concept

Visual Aid for discussion & evaluation

Read more

Prototype Engineering

Simulates ABS,
PE, Rubber ......

Read more

Functional Engineering

Products that outperforms conventional manufacturing

Coming Soon

Specialty

Specific workflow, Specific application, …

Read more

Material Properties Table

For MSLA Printer Resins

 
 
MODELING
GRAY
 
MODELING
DENTAL
 
MODELING
CLEAR
 
CASTABLE
CYAN
Group
Tensile(MPa) 52 - 60 47 - 55 53 - 67 6 - 7
Elongation(%) 2 - 4 1 - 4 1 - 3 7 - 9
Impact(J/m) 20 - 28 18 -26 29 -31 -
Hardness(Shore) 89 - 92D 86 - 90D 85 - 88D -
Flexure Strength(MPa) 92 - 100 92 - 96 95 - 105 6 - 8
Flexure Modulus(MPa) 2100 - 2300 2100 - 2300 1800 - 2000 90 - 120
HDT(°F/°C) 140.36/60.2 137.84/58.8 149.54/65.3 -
Viscosity(cP) 310 - 380 300 - 370 360 - 450 300 - 350

 


 

 
 
HEAT
GRAY
 
EXPERT
GRAY
 
RIGID
DUSTY OLIVE
 
SPRING
BLACK
 
SPRING
PINK
Group
Post-curing FormCure at
35℃/60min
FormCure at
60℃/60min + oven 160℃/90min
- - - -
Tensile(MPa) 55 - 75 60 - 80 65 - 74 55 - 60 1.2 - 1.8 1.2 - 1.8
Elongation(%) 1 - 2 1 - 3 3 - 6 8 - 12 45 - 65 50 - 70
Impact (J/m) 19 - 25 24 - 31 25 - 27 40 - 45 - -
Hardness (Shore) 85 - 87 D 87 - 89 D 91 - 93 D 89 - 92D 57 - 62A 58 - 62A
Flexure strength (MPa) 130 - 145 135 - 185 110 - 130 85 - 100 - -
Flexure modulus (MPa) 2550 - 2650 2850 - 3000 2200 - 2400 1600 - 1800 - -
HDT (℉/℃) 228.2/109 482/250 * 160.9/71.6 147.4/64.1 - -
Viscosity (cP) 450 - 550 600 - 700 650 - 800 480 - 520 480 - 520
  * FormCure at 80℃/120min + oven 160℃/180min        
25℃ density(g/cm3)(cP) - - - - 1.11 - 1.12 1.11 - 1.12
Tear Strength (kN/m) - - - - 3 - 5 3 - 5
Compression (%) - - - - 1 - 2 1 - 2
Layer thickness(um) - - 0.1 mm - - -
PostCure method) - - Elegoo Mercury 30 min - - -

Item Price Includes Free Shipping to the 48 Continental U.S. States

×
×