Material Properties Table
For MSLA Resins: Design Concept
|
MODELING
GRAY |
MODELING
DENTAL |
MODELING
CLEAR |
CASTABLE
CYAN |
|
| Group | ||||
|---|---|---|---|---|
| Tensile(MPa) | 52 - 60 | 47 - 55 | 53 - 67 | 6 - 7 |
| Elongation(%) | 2 - 4 | 1 - 4 | 1 - 3 | 7 - 9 |
| Impact(J/m) | 20 - 28 | 18 -26 | 29 -31 | - |
| Hardness(Shore) | 89 - 92D | 86 - 90D | 85 - 88D | - |
| Flexure Strength(MPa) | 92 - 100 | 92 - 96 | 95 - 105 | 6 - 8 |
| Flexure Modulus(MPa) | 2100 - 2300 | 2100 - 2300 | 1800 - 2000 | 90 - 120 |
| HDT(°F/°C) | 140.36/60.2 | 137.84/58.8 | 149.54/65.3 | - |
| Viscosity(cP) | 310 - 380 | 300 - 370 | 360 - 450 | 300 - 350 |
|
HEAT
GRAY |
EXPERT
GRAY |
RIGID
DUSTY OLIVE |
SPRING
BLACK |
SPRING
PINK |
||
| Group | ||||||
|---|---|---|---|---|---|---|
| Post-curing | FormCure at 35℃/60min |
FormCure at 60℃/60min + oven 160℃/90min |
- | - | - | - |
| Tensile(MPa) | 55 - 75 | 60 - 80 | 65 - 74 | 55 - 60 | 1.2 - 1.8 | 1.2 - 1.8 |
| Elongation(%) | 1 - 2 | 1 - 3 | 3 - 6 | 8 - 12 | 45 - 65 | 50 - 70 |
| Impact (J/m) | 19 - 25 | 24 - 31 | 25 - 27 | 40 - 45 | - | - |
| Hardness (Shore) | 85 - 87 D | 87 - 89 D | 91 - 93 D | 89 - 92D | 57 - 62A | 58 - 62A |
| Flexure strength (MPa) | 130 - 145 | 135 - 185 | 110 - 130 | 85 - 100 | - | - |
| Flexure modulus (MPa) | 2550 - 2650 | 2850 - 3000 | 2200 - 2400 | 1600 - 1800 | - | - |
| HDT (℉/℃) | 228.2/109 | 482/250 * | 160.9/71.6 | 147.4/64.1 | - | - |
| Viscosity (cP) | 450 - 550 | 600 - 700 | 650 - 800 | 480 - 520 | 480 - 520 | |
| * FormCure at 80℃/120min + oven 160℃/180min | ||||||
| 25℃ density(g/cm3)(cP) | - | - | - | - | 1.11 - 1.12 | 1.11 - 1.12 |
| Tear Strength (kN/m) | - | - | - | - | 3 - 5 | 3 - 5 |
| Compression (%) | - | - | - | - | 1 - 2 | 1 - 2 |
| Layer thickness(um) | - | - | 0.1 mm | - | - | - |
| PostCure method) | - | - | Elegoo Mercury 30 min | - | - | - |