MODELING
200 GRAY |
MODELING
BLACK V2 |
MODELING
CLEAR |
MODELING
GRAY |
MODELING
WHITE |
MODELING
TAN |
|
| Group | ||||||
|---|---|---|---|---|---|---|
| Tensile(MPa) | 57-59 | 47-52 | 53-63 | 50-55 | 46-53 | 40-44 |
| Elongation(%) | 3-7 | 2-6 | 1-4 | 2-4 | 1-3 | 2-6 |
| Impact(J/m) | 43-44 | 16-22 | 17-29 | 15-17 | 23-27 | 15-17 |
| Hardness(Shore) | 86-88D | 86-88D | 85-88D | 85-87D | 85-90D | 84-86D |
| Flexure Strength(MPa) | 92-104 | 82-86 | 89-105 | 89-95 | 90-105 | 79-83 |
| Flexure Modulus(MPa) | 1700-2000 | 2050-2150 | 1600-2000 | 2250-2470 | 1550-1750 | 1970-2190 |
| HDT(°F/°C) | 138.02/58.9 | 135.86/57.7 | 170.60/77.0 | 135/57 | 170.78/77.1 | 131/55 |
| Viscosity(cP) | 675-825 | 1000-1200 | 1100-1300 | 1000-1300 | 900-1050 | 1000-1200 |
| Compression Set(%) | - | - | - | - | - | - |
|
HEAT
CHAMPAGNE |
EXPERT
BLACK |
EXPERT
GRAY |
EXPERT
TAN |
ROBUST
CHAMPAGNE |
SPRING
BLACK |
SPRING
PINK |
||
| Group | ||||||||
|---|---|---|---|---|---|---|---|---|
| Post-curing | FormCure at 60℃/60min |
FormCure at 60℃/60min + oven 160℃/90min |
- | FormCure 60°C, 60min | FormCure 60°C, 60min | - | - | - |
| Tensile(MPa) | 65 - 80 | 65 - 85 | 70-80 | 62-68 | 60-68 | 45-55 | 1.2-1.3 | 1.1-1.2 |
| Elongation(%) | 1-3 | 1-2 | 1-3 | 3-7 | 2-4 | 10-21 | 45-55 | 40-55 |
| Impact (J/m) | 16 - 27 | 23 - 39 | 35-40 | 27-33 | 19-22 | 60-65 | - | - |
| Hardness (Shore) | 86-88 D | 86-88 D | 88-90 D | 91-93 D | 89-91 D | 83-86 D | 57-60 A | 56-59 A |
| Flexure strength (MPa) | 140-160 | 150-180 | 115-150 | 114-118 | 124-128 | 65-90 | - | - |
| Flexure modulus (MPa) | 2550-2750 | 2950-3100 | 2050-2500 | 1980-2050 | 2090-2130 | 1000-1500 | - | - |
| HDT (℉/℃) | 213.8/101 | 370.4/188 * | 154.04/67.8 | 161.8/72.1 | 166.8/74.9 | 125.78/52.1 | - | - |
| Viscosity (cP) | 550-650 | 1050-1200 | 550-660 | 550-650 | 1300-1500 | 500-600 | 480-550 | |
| * FormCure at 80℃/120min + oven 160℃/180min | ||||||||
| Compression Set(%) | - | - | - | - | - | - | 1.5-2.5 | 1.5-2.5 |
| Layer thickness(um) | - | - | - | 0.1 mm | 0.1 mm | - | - | - |